Z1261P PID Free

Item code	Specification of thickness(mm)	Specification of width (mm)	Gram weight (g/sqm)	Length/roll (m)	ackage means (mm)	Min order quantity（sqm)
Z1261P	0.50	500-1200	420-450	100	-	2,000
	0.45	360	370-400	120	-	2,000
	0.45	550	370-400	120	560290300	2,000
	0.45	680	370-400	120	690290300	2,000
	0.45	810	370-400	120	830290300	2,000
	0.45	985	370-400	120	1010290300	2,000
	0.45	990	370-400	120	1010290300	2,000
	0.45	1000	370-400	120	1010290300	2,000
	0.45	1020	370-400	120	1040290300	2,000
	0.45	1060	370-400	120	1080290300	2,000
	0.40	500-1200	320-340	150	-	3,000
	0.35	500-1200	280-300	170	-	3,000
	0.30	500-1200	230-250	200	-	3,000

Item			Test method	Unit	Fast cure type
					Z1261A	Z1261 / Z1261P	Z1261C
Density			ISO1183	g/cm³	0.95	0.95	0.95
content			TGA	％	26-33	26-33	28-33
Softening point			DSC	℃	55	55	55
Surface hardness			GB/T531-1999	Shore A	65	65	62
Tensile strenghth (after crosslinking)			ISO527-3	MPa	20	20	20
Elongation (after crosslinking)				%	600	600	600
Strenghth of Extension				MPa	6	6	6
UV cutoff wavelength			UV-vis	Nm	--	360	360
Optical transmission			GB2410-80	%	91.5	91	91
Refractive index			ISO489	--	1.480	1.482	1.482
（0.45MM; 120℃，3min） Thermal shrinkage			Q/ZX001-2012	MD%	≤3.0	≤3.0	≤10.0
				TD%	≤1.0	≤1.0	≤3.0
（140℃，17min） Cross-linking rate			Q/ZX001-2012	Gel %	≥75.0
Peeling strength		With Glass	Q/ZX001-2012	N/cm	>60
		With TPT		N/cm	>40
(90℃,90%RH, 1500hrs) Damp Heat resistance	Yellowness index		Q/ZX001-2012	△YI	<3
	Peeling strenghth with glass			N/cm	＞40
(1500hrs) UV Exposure resistance	Yellowness index		Q/ZX001-2012	△YI	<3
	Peeling strenghth with glass			N/cm	＞40
Volume resistance			GB/T 1410	Ω·cm	≥1*1015
Dielectric strength			GB/T1408.1	Kv/mm	＞28
PID resistance test (85℃,85%RH,-1000V,96H)			IEC61730-2:2004 IEC61215:2005	Power loss %	<5%

Operating parameters Items		Extra fast cure, High transmission, PID free
		Z1261 / Z1261A /Z1261P
Laminating curing parameters		135±2	140±2	145±2	150±2
	Heating panel (℃)

	Pump down time (min)	5±1	5±1	4±1	4±1
	Holding time(min)	15±2	12±1	10±1	7±1

Note: Laminating process conditions shall be selected and confirmed according to the performance of laminating machine.